品牌:赛福
金属化薄膜:4um-12um
锌铝膜:4.8*50*2.5
安全膜:5.8*37.5*1.5
起订:1kg
供应:100000kg
发货:3天内
n 镀层形式Types of metalized Layer：
n 产品Products：
|
Ø 铝金属化聚丙烯薄膜 Ø 铝金属化聚丙烯安全膜 Ø 边缘加厚锌铝金属化聚丙烯薄膜 Ø 边缘加厚锌铝金属化聚丙烯安全膜 Ø 边缘加厚渐变方阻锌铝金属化聚丙烯薄膜 Ø 铝金属化聚酯薄膜 Ø 边缘加厚锌铝金属化聚酯薄膜 |
Ø Aluminum metalized polypropylene film. Ø Aluminum metallized polypropylene safety film. Ø Zinc – Aluminum alloy metallized polypropylene film with heavy edge. Ø Zinc – Aluminum alloy metallized polypropylene safety film with heavy edge. Ø Zinc – Aluminum alloy metallized polypropylene film with heavy edge and gradient square resistance. Ø Aluminum metalized polyester film. Ø Zinc – Aluminum alloy metallized polyester film with heavy edge. |
n 卷芯Cores：
|
Ø 材质：塑料 Ø 宽度：膜宽度偏差±0.3mm Ø 内直径：75mm +1.0mm/-0.5mm |
Ø Material：Plastic. Ø Width：Film Slit Width ±0.3mm. Ø Inner Diameter：75mm +1.0mm/-0.5mm. |
n 膜卷的外直径Roll Outer Diameter：
|
分切宽度W Slit widths |
推荐外直径D Recommend outer diameter |
|
4.5mm≤W＜10mm |
140mm≤D≤185mm |
|
10mm≤W＜25mm |
150mm≤D≤185mm |
|
25mm≤W＜50mm |
150mm≤D≤240mm |
|
50mm≤W |
150mm≤D≤350mm |
n 金属化膜技术参数Specifications of metallized film：
金属化聚丙烯薄膜(MPP Film)：
|
性能 Properties |
单位 Unit |
要求 Requirements |
|
|
密度Density |
g/cm3 |
0.905±0.005 |
|
|
厚度 Thickness |
µm |
3.8 ~ 15 |
|
|
抗拉强度 Tensile Strength |
纵向MD (MPa) |
≥100 |
|
|
断裂伸长率 Elongation at Break |
纵向MD (%) |
40 ~ 200 |
|
|
热收缩率 Heat Shrinkage |
纵向MD (%) |
≤5 ( 120°C, 10min) ( 120°C , 10 min ) |
|
|
介电强度Break-dowm voltage |
V/µm |
≥350 ( 23°C, DC ) |
|
|
镀层方块电阻 Coating square resistance |
Ω/□ |
有加厚区 (with heavy-edge ) |
加厚区方阻(heavy-edge area)：3±1 非加厚区方阻(non heavy-edge area)：（6～20）渐变 |
|
无加厚(without heavy-edge) |
（2～20）渐变 |
||
|
介电损耗因数 Dissipation Factor |
- |
≤4×10-4 (20℃，1KHz ) |
|
|
RC值 |
ΩF |
≥5×104 |
|
金属化聚酯薄膜(MPET Film)：
|
性能 Properties |
单位 Unit |
要求 Requirements |
||||||
|
密度Density |
g/cm3 |
1.34 |
||||||
|
厚度 Thickness |
µm |
＜5 |
5～12 |
＞12 |
||||
|
抗拉强度 Tensile Strength |
纵向MD (MPa) |
≥84 |
≥108 |
≥120 |
||||
|
断裂伸长率 Elongation at Break |
纵向MD (%) |
≥22 |
≥33 |
≥44 |
||||
|
介电强度 Break-dowm voltage |
V/µm |
≥200 ( 23°C, DC ) |
≥250 ( 23°C, DC ) |
|||||
|
热收缩率 Heat Shrinkage |
纵向MD (%) |
≤3 ( 120°C, 10min) |
||||||
|
镀层方块电阻 Coating square resistance |
Ω/□ |
铝膜Al |
1.5±0.5 |
2.0±0.5 |
2.5±0.5 |
3±1 |
||
|
锌铝膜Zn/Al |
（6～7.5）±30% |
|||||||
|
介电损耗因数 Dissipation Factor |
- |
≤60×10-4 (20℃，1KHz ) |
||||||
|
RC值 |
ΩF |
≥1×104 |
||||||
n 包装Packing
|
Ø 膜卷用塑料袋包装，抽真空后放入干燥剂热封 Ø 塑料包装袋外贴标签标明型号，厚度，宽度，留边宽度和电阻 |
Ø Roll films are packed in vacuum plastic bag and heat-sealed with desiccants. Ø Bags are marked with lables of types , thickness, Ø width, free margin width and resistance. |
|
Ø 塑料袋外面用纸箱包装 Ø 纸箱外面用木箱包装或者加固纸箱 |
Ø The bags are packed in carton cases. Ø The cartons are wrapped in wooden cases or reinforced carton. |
n 储存Storge
|
Ø 金属化膜在使用之前应该按原包装保存。环境温度应该控制在5～35℃，湿度小于85%RH。 Ø 金属层暴露在潮气中会很容易发生氧化。因此，包装打开后，膜卷应该尽快使用。 Ø 建议打开包装的膜卷应该保存的温度条件是15～25℃，湿度小于60%RH。 Ø 金属化膜若保持原密封包装，并储存在如上所述的环境下，那么其储存期限可以满足下列条件： 铝金属化薄膜：从交付日起12个月。 锌铝金属化薄膜：因为锌相当不稳定，储存的期限取决薄膜的电阻： 小于等于10 Ohms：6个月（从交付日起） 10 Ohms到15 Ohms：3个月（从交付日起） 15 Ohms以上：1个月（从交付日起） |
Ø metallized film should be stored in its original package until its use with temperature 5 ～ 35℃ and humidity less than 85%RH. Ø metallized layer is easily oxidized when exposure to moisture. Therefore, the film should be used as soon as possible when opened.
Ø The recommended temperature is 15 -25℃ with humidity less than 60%RH after the package is open.
Ø With original sealed package, and stored in the above mentioned conditions, the storage time can be as following: Al metalized Film: 12 months from the delivered date.. Al/Zn Alloy metalized Film: As Zn is relatively unstable, preservation period depends on the resistance of the film: Less than 10 Ohms: 6 months (from delivery date)
10 Ohms to 15 Ohms: 3 months (from delivery date)
15 Ohms: 1months (from delivery date) |